Temperature effect on the porosity of hydroxyapatite scaffolds and its use in tissue engineering

Vista sencilla de ítem
dc.creatorZarate-Córdova, Vareska Lucero
dc.creatorOropeza-Guzmán, Mercedes Teresita
dc.creatorLópez-Maldonado, Eduardo Alberto
dc.creatorIglesias, Ana Leticia
dc.creatorNg, Theodore
dc.creatorSerena-Gómez, Eduardo
dc.creatorPérez-González, Graciela Lizeth
dc.creatorVillarreal-Gómez, Luis Jesús
dc.date2020-12-29
dc.descriptionThe search for a suitable bone replacement is of great importance due to the difficulty to use autologous transplants. Hence, the objective of this work is to compare the temperature effect on the porosity and average pore diameter of hydroxyapatite porous scaffolds fabricated by the salt leaching method.  Hydroxyapatite porous scaffolds fabricated by the salt leaching technique were sintered from ~150 to 1000 °C. Synthesized hydroxyapatite was assessed by X-ray diffraction (XRD). Zeta potential at different temperatures was evaluated. Specimens were characterized using scanning electron microscopy (SEM) and Raman analysis. The results showed that significant porosity (57%) and pore size (49 µm) occurred with a thermal treatment above ~ 850 °C for scaffolds that were pre-sintered at 1050 °C.en-US
dc.descriptionLa búsqueda de un reemplazo óseo adecuado es de gran importancia debido a la dificultad de utilizar trasplantes autólogos. Es por esto, que el objetivo de este trabajo es comparar el efecto de la temperatura sobre la porosidad y el diámetro promedio de poro fabricados con el método de lixiviación de sales, siendo sinterizados desde ~150 a 1000 °C. Los andamios fabricados de hidroxiapatita fueron evaluados con difracción de rayos X (XRD). El potencial zeta fue evaluado a diferentes temperaturas. Los especímenes fueron caracterizados utilizando microscopia electrónica de barrido (SEM) y análisis Raman. Los resultados mostraron que la porosidad importante (57%) y tamaño de poro (49 µm) ocurren con un tratamiento térmico superior a ~ 850 °C para andamios que fueron pre-sinterizados a 1050 °C.es-ES
dc.formatapplication/pdf
dc.formattext/html
dc.formattext/xml
dc.identifierhttps://recit.uabc.mx/index.php/revista/article/view/66
dc.identifier10.37636/recit.v34213221
dc.languageeng
dc.publisherUniversidad Autónoma de Baja Californiaen-US
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/66/189
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/66/190
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/66/191
dc.rightsCopyright (c) 2020 Vareska Lucero Zarate-Córdova, Mercedes Teresita Oropeza-Guzmán, Eduardo Alberto López-Maldonado, Dra. Ana Leticia Iglesias, Theodore Ng, Eduardo Serena-Gómez, Dra. Graciela Lizeth Pérez González, Luis Jesús Villarreal-Gómezen-US
dc.rightshttp://creativecommons.org/licenses/by/4.0en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 3 No. 4 (2020): October-December; 213-221en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 3 Núm. 4 (2020): Octubre-Diciembre; 213-221es-ES
dc.source2594-1925
dc.subjectHydroxyapatiteen-US
dc.subjectporous scaffolden-US
dc.subjectsalt leaching methoden-US
dc.subjectHidroxiapatitaes-ES
dc.subjectandamios porososes-ES
dc.subjectmétodo de lixiviación de saleses-ES
dc.titleTemperature effect on the porosity of hydroxyapatite scaffolds and its use in tissue engineeringen-US
dc.titleEfecto de la temperatura sobre la porosidad de andamios de hidroxiapatita y su uso en ingeniería de tejidoses-ES
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
Archivos
Colecciones
Revista de Ciencias Tecnológicas