Reduction of ferrite phase in austenitic stainless steels by controlling content of Cr-Ni equivalent

Vista sencilla de ítem
dc.creatorRuiz Ochoa, Juan Antonio
dc.creatorRamos Azpeitia, Mitzuo Osvaldo
dc.creatorCastañeda Robles, Iván Erick
dc.creatorHernández Rivera, José Luis
dc.creatorPaz González, Juan Antonio
dc.date2020-08-13
dc.descriptionAISI 316L austenitic stainless steels are very common in the industry. Large amounts of this material are discarded as a chisel and can subsequently be used as recycled material for casting. In marine environments (highly corrosive), this type of steel presents intragranular corrosion, specifically in one of its phases, in the ferrite, so it is preferred to keep it at the lowest possible proportion (<1%), but usually it is found around the 12% of it. If a casting is required to transport a pressurized fluid from AISI 316L steel, it should be performed according to considerations described in ASTM A351 Standard.  We find that CF3M steel is the most similar in terms of elemental chemical proportions of its components. Therefore, the Schaeffler and Schoefer diagrams were used to reduce the content of "equivalent ferrite" by at least 90%, making adjustments in the casting by modifying the Ni and Cr percentages.en-US
dc.descriptionLos aceros inoxidables austeníticos AISI 316L son muy comunes en la industria. Grandes cantidades de este material se desechan como chatarra y pueden utilizarse posteriormente como material reciclado para la colada. En ambientes marinos (altamente corrosivos), este tipo de acero presenta corrosión intragranular, específicamente en una de sus fases, en la ferrita, por lo que se prefiere mantenerla en la menor proporción posible (<1%), pero normalmente se encuentra alrededor del 12%. Si se requiere que una pieza de fundición de acero AISI 316L transporte un fluido presurizado, debe realizarse de acuerdo con las consideraciones descritas en la norma ASTM A351. En este trabajo, se encontró que el acero CF3M tiene mayor solicitud en términos de proporciones químicas elementales de sus componentes. Por lo tanto, se utilizaron los diagramas de Schaeffler y Schoefer para reducir el contenido de "ferrita equivalente" en al menos el 90%, haciendo ajustes en la fundición modificando los porcentajes de Ni y Cr.es-ES
dc.formatapplication/pdf
dc.formattext/html
dc.formatapplication/xml
dc.identifierhttps://recit.uabc.mx/index.php/revista/article/view/42
dc.identifier10.37636/recit.v23113117
dc.languagespa
dc.publisherUniversidad Autónoma de Baja Californiaen-US
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/42/66
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/42/86
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/42/172
dc.rightsCopyright (c) 2019 Juan Antonio Ruiz Ochoa, Mitzuo Osvaldo Ramos Azpeitia, Iván Erick Castañeda Robles, José Luis Hernández Rivera, Juan Antonio Paz Gonzálezen-US
dc.rightshttp://creativecommons.org/licenses/by/4.0en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 2 No. 3 (2019): July-September; 113-117en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 2 Núm. 3 (2019): Julio-Septiembre; 113-117es-ES
dc.source2594-1925
dc.subjectAustenitic Stainless Steelsen-US
dc.subjectFerriteen-US
dc.subjectSchaeffler Diagramen-US
dc.subjectSchoefer Diagramen-US
dc.subjectAceros Inoxidables Austeníticoses-ES
dc.subjectFerritaes-ES
dc.subjectDiagrama de Schaefferes-ES
dc.subjectDiagrama de Schoeferes-ES
dc.titleReduction of ferrite phase in austenitic stainless steels by controlling content of Cr-Ni equivalenten-US
dc.titleReducción de la fase de ferrita en aceros inoxidables austeníticos mediante el control del contenido de equivalentes de Cr-Nies-ES
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.typeResearch articleen-US
dc.typeArtículo de investigaciónes-ES
Archivos
Colecciones
Revista de Ciencias Tecnológicas