dc.descriptionIn this work, we synthesized the alloy of nickel‒copper by thermal treatment in reductive‒flow of hydrated salts based on Ni and Cu used the stoichiometric 3:1 respectively. The methodology proposed is low‒cost, simple, friendly to environment, and obtain a crystalline phase free of contaminants or remnants of reaction with crystal size of 33 nm and particle size of 659 ± 123 x 416 ± 102 nm, the particles exhibit like‒spherical morphology and heterogeneous agglomerates. In addition, we compared the experimental lattice parameters by theoretical reported and calculated by Vegard's law. The results by Vegard´s law suggest that the composition of copper (XCu) in the alloy is different with respect to the phase identified Ni0.76Cu0.24 by XRD database, but this result don’t affect the lattice parameter. The material was characterized by X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), scanning electron microscopy (SEM), and crystal size and copper fraction in alloy was estimated using the Scherrer equation, and Vegard´s law respectively.en-US
dc.descriptionEn este trabajo se propone la síntesis de una aleación de níquel‒cobre por descomposición térmica en atmósfera reductora a partir de la mezcla estequiometrica 3:1 de sales de Ni y Cu. La metodología utilizada es de bajo costo, sencilla, amigable con el medio ambiente y permite obtener una fase cristalina libre de contaminantes o remanentes de reacción con un tamaño de cristal de 33 nm y tamaño de partícula de 659 ± 123 x 416 ± 102 nm, con morfología semiesférica y aglomerados heterogéneos. Adicionalmente al realizar un análisis comparativo de los parámetros de red experimental, teóricos reportados y calculados con la ley de Vegard, sugiere que el material sintetizado presenta una fracción diferente de Cu con respecto a la identificada por la base de datos Ni0.76Cu0.24, sin embargo, en el parámetro de red no se observa un cambio significativo (≈0.1 %). El material se caracterizó por difracción de rayos-X (XRD), espectroscopía por dispersión de energía (EDS) y microscopía electrónica de barrido (SEM), el tamaño de cristal se calculó con la ecuación de Scherrer y la fracción de Cu en la aleación con aplicando la ley de Vegard.es-ES
dc.formatapplication/pdf
dc.formattext/html
dc.formatapplication/xml
dc.identifierhttps://recit.uabc.mx/index.php/revista/article/view/53
dc.identifier10.37636/recit.v21813
dc.languagespa
dc.publisherUniversidad Autónoma de Baja Californiaen-US
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/53/96
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/53/104
dc.relationhttps://recit.uabc.mx/index.php/revista/article/view/53/133
dc.rightsCopyright (c) 2019 ​Flores Sánchez Luis Antonio, Quintana Melgoza Juan Manuelen-US
dc.rightshttp://creativecommons.org/licenses/by/4.0en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 2 No. 1 (2019): January-March; 8-13en-US
dc.sourceREVISTA DE CIENCIAS TECNOLÓGICAS; Vol. 2 Núm. 1 (2019): Enero-Marzo; 8-13es-ES
dc.source2594-1925
dc.subjectSynthesisen-US
dc.subjectReductive Thermal Decompositionen-US
dc.subjectCharacterizationen-US
dc.subjectAlloyen-US
dc.subjectNickel-Copper.en-US
dc.subjectSíntesises-ES
dc.subjectDescomposición Térmica Reductoraes-ES
dc.subjectCaracterizaciónes-ES
dc.subjectAleaciónes-ES
dc.subjectNíquel-Cobre.es-ES
dc.titleSynthesis and characterization of crystalline Ni0.76Cu0.24en-US
dc.titleSíntesis y caracterización de Ni0.76Cu0.24 cristalinoes-ES
dc.typeinfo:eu-repo/semantics/article
dc.typeinfo:eu-repo/semantics/publishedVersion
dc.typeResearch articleen-US
dc.typeArticulo de Investigaciónes-ES
Archivos
Colecciones
Revista de Ciencias Tecnológicas